I7.04 - Stress, Deformation, and Fracture of High-Capacity Anodes 
Date/Time:
April 9, 2015   9:45am - 10:00am
 
Speaker:
 
Taxonomy
 
 
 
 
 
Share:
 

We have performed a number of experiments to examine the mechanical behavior of high capacity anodes. In particular, using two separate techniques, we have measured the fracture energy of lithiated silicon thin-film electrodes as a function of lithium concentration. The fracture energy is found to be similar to that of pure silicon and essentially independent of the concentration of lithium. Thus, while lithiated silicon can flow plastically, it appears to fracture in a brittle manner. Additionally, we have measured stresses that develop during lithiation/delithiation of germanium electrodes. We have performed complementary XRD experiments to determine the phases that develop during lithiation/delithiation. These measurements demonstrate plastic flow in germanium, which limits the stresses, thus reducing the driving force for crack propagation. Overall, these experiments provide key insight into the development of high-capacity anode systems that avoid fracture and thereby enable long cycle life.
 


 
 
Average Rating: (No Ratings)
  Was great, surpassed expectations, and I would recommend this
  Was good, met expectations, and I would recommend this
  Was okay, met most expectations
  Was okay but did not meet expectations
  Was bad and I would not recommend this
 



Submit
 
Group III-Sb Metamorphic Buffer on Si for p-Channel all-III-V CMOS: Electrical Properties, Growth and Surface Defects
Kinetics and Structure of Nickelide Contact Formation to InGaAs Fin Channels
Recent Progress in Understanding the Electrical Reliability of GaN High-Electron Mobility Transistors
The Effect of ALD Temperature on Border Traps in Al2O3 InGaAs Gate Stacks
Atomic Layer Deposition of Crystalline SrHfxTi1-xO3 Directly on Ge (001) for High-K Dielectric Applications