CC4.02 - Intermetallic Clathrates based on Ba-Ga-Sn as for Bulk Thermoelectric Materials without Toxic Elements 
Date/Time:
December 2, 2014   8:30am - 9:00am
 
Taxonomy
 
 
 
Share:
 

Intermetallic clathrates are the representative of nano-cage structured material showing low thermal conductivity [1]. A dimorphic clathrate Ba8Ga16Sn30possesses type-I and type-VIII structures. The type-I phase transforms to the type-VIII phase on heating above 739 K. The type-I compound displays the glasslike thermal conductivity with a plateau at 4-12 K, which is ascribed to the strong interaction of acoustic phonons with the low-energy off-center rattling mode. In the type-VIII compound, the Ba guest is vibrating nearly on center of the distorted dodecahedron. Nevertheless, the thermal conductivity is as low as 0.7W/Km for T> 300 K. The carrier type and its density in single crystals can be tuned by controlling the initial amount of flux, Ga or Sn. Further optimization of carrier density by alloying has led to high ZT of 1.0 and 1.45 for p- and n-type, respectively, at around 500 K, where the conventional materials based on Bi-Te and Pb-Te had a valley in ZT. By assembling p- and n-type legs made of Ba8Ga16Sn30, a module was prepared with the segments of Bi-Te legs. The conversion efficiency reached 7.5% at the temperature difference of 390 K.

Reference:

[1] T. Takabatake et al., Rev. Mod. Phys. 86, 669-716 (2014).
 


 
 
Average Rating: (No Ratings)
  Was great, surpassed expectations, and I would recommend this
  Was good, met expectations, and I would recommend this
  Was okay, met most expectations
  Was okay but did not meet expectations
  Was bad and I would not recommend this
 



Submit
 
Harvesting Waste Heat Recovery by Electrochemical Systems
Phonon Transport in SiGe-Based Nanocomposites and Nanowires for Thermoelectric Applications
Essentials of Getting Your Work Published
Performance Enhancement of Pentacene Based Organic Field-Effect Transistor through DNA Interlayer
Semiconducting Polymer-Dipeptide Nanostructures by Ultrasonically-Assisted Self-Assembling