D9.02 - Photocurrent Enhancement in BiVO Photoanode Decorated with Ag/SiO Core-Shell Nanoparticles 
Date/Time:
April 25, 2014   8:30am - 8:45am
 
Speaker:
 
Taxonomy
 
 
 
Share:
 

BiVO has emerged as one of the most promising photoanode materials for solar water splitting. The breakthrough is the result of the successful identification of the performance limiting factors in the material: (i) poor catalytic activity and (ii) slow electron transport (low carrier separation efficiency). The first problem is solved by coupling water oxidation co-catalysts on the surface of BiVO, while the latter is overcome by introducing dopants, such as W and Mo. We recently showed that this can be further improved by introducing a gradient in the W dopant concentration in BiVO, which has resulted in carrier separation efficiencies as high as 80%. As a result, water oxidation catalysis and bulk carrier recombination no longer limit the photocurrent of BiVO. Instead, modest light absorption—especially for photons with energy close to the bandgap—becomes the main limitation. To illustrate this, the amount of light absorbed in our best W:BiVO samples is ~5 mA/cm, compared to a theoretical maximum of ~7.5 mA/cm (assuming that all photons with an energy higher than the bandgap are absorbed and collected). This means that a significant increase of the photocurrent (up to 2.5 mA/cm) can be achieved when the light absorption is improved.In this work, we explore the application of core-shell nanoparticles on the surface of 100 nm-thick spray-deposited BiVO films as a route to enhance the optical absorption of the films by near-field plasmonic enhancement. Similar to the work of Thomann et al., SiO is used as the shell layer to avoid surface recombination. However, here, Ag is used as a core material because: (i) Ag is less expensive than Au, and (ii) the plasmon frequency of Ag can be tailored between 400 to 550 nm, which is a better match with the absorption spectrum of BiVO. Under back-side AM1.5 illumination, we achieve a ~2.5 fold photocurrent improvement when decorating BiVO with Ag/SiO core-shell nanoparticles. We show that this enhancement can be attributed to two factors introduced by the core-shell nanoparticles. The first factor is related to the improved optical absorption in the layer, caused by both the optical near-field enhancement and improved light scattering (also called far-field effects) induced by the excitation of localized surface plasmon resonance in Ag nanoparticles. In addition, a significant non-optical enhancement is also observed, which is tentatively attributed to the reduction of surface recombination.References1. F. F. Abdi and R. van de Krol, J Phys. Chem. C 116 (2012) 93982. D. K. Zhong, S. Choi and D. Gamelin, J Am. Chem. Soc. 133 (2011) 183703. F. F. Abdi, N. Firet and R. van de Krol, ChemCatChem 5 (2013) 4904. S. K. Pilli et al., Energy Environ. Sci. 4 (2011) 50285. F. F. Abdi et al., Nat. Commun. 4:2195 (2013) 16. I. Thomann et al., Nano Letters 11 (2011) 3440
 


 
 
Average Rating: (No Ratings)
  Was great, surpassed expectations, and I would recommend this
  Was good, met expectations, and I would recommend this
  Was okay, met most expectations
  Was okay but did not meet expectations
  Was bad and I would not recommend this
 



Submit
 
Keynote Address
Panel Discussion - Different Approaches to Commercializing Materials Research
Business Challenges to Starting a Materials-Based Company
Fred Kavli Distinguished Lectureship in Nanoscience
Application of In-situ X-ray Absorption, Emission and Powder Diffraction Studies in Nanomaterials Research - From the Design of an In-situ Experiment to Data Analysis